IPS e.max® ZirCAD Prime

This revolutionary material provides exceptional quality and aesthetics and covers a wide range of dental indications - from single crowns to 14-point bridges. IPS ZirCAD Prime is a 'One-Disc Solution': the material allows achieving the highest quality results while optimizing the efficiency and costs of dental laboratories. Gradient Technology (GT) represents a new, unique production method.

Technical Specifications:

• Flexural strength:
• 5Y-TZP (upper disc layer): 650 MPa1
• 3Y-TZP (lower disc layer): 1200 MPa1
• Maximum possibilities: staining, cut-back, layering and infiltration technique
• Available colors: A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4, BL1, BL2, BL3, BL4

IPS e.max® ZirCAD MO

IPS e.max ZirCAD MO has been developed for use in classic veneering technique. Even heavily discolored stumps and metal inserts can be effectively hidden due to the increased opacity of the material.

Technical Specifications:

• Indications: crown and bridge frameworks
• Implant-supported structures
• Processing techniques: veneering, press-on veneering, CAD-on
• Available colors: MO-0, MO-1, MO-2, MO-3, MO-4

IPS e.max® ZirCAD LT

IPS e.max ZirCAD LT is the most versatile material in the portfolio. It combines high mechanical strength (1200 MPa) with natural aesthetics.

Technical Specifications:

• Mechanical strength: 1200 MPa
• Indications: anatomical crowns, bridges, implant structures
• Processing techniques: glazing, characterization, infiltration, veneering
• Available colors: A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4, BL

IPS e.max® CAD CEREC®/inLab®

IPS e.max® CAD is a lithium disilicate glass-ceramic used in dentistry that combines exceptional aesthetics with durability, making it perfect for prosthetic restorations such as crowns, veneers, inlays, and onlays. This material works great for full-contour work. It has a wide range of processing options, high biaxial flexural strength - 530MPa[2], and high fracture toughness 2.11 MPa m1/2[3]

Technical Specifications:

• IPS e.max CAD HT (High Translucency) - highly translucent block, dedicated for smaller restorations like inlay/onlay
• IPS e.max CAD MT (Medium Translucency) - medium translucency block, used for restorations requiring more brightness than HT restorations
• IPS e.max CAD LT (Low Translucency) - low translucency block, suitable for most restorations
• IPS e.max CAD MO (Medium Opacity) - block shows particular opacity recommended for frameworks on slightly discolored stumps
• Available colors: BL1, BL2, BL3, BL4, A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4

Remanium Star Powder

Specialized CoCr dental alloy designed for the production of crown, bridge, and skeletal prosthesis structures in laser sintering technology.

Technical Specifications:

• Composition: Co-60.5%, Cr-28.0%, W-9.0%, Si-1.5%
• Tensile strength: 1170 MPa
• Hardness: 395 HV10
• CTE(25-500°C): 14.4x10⁻⁶K⁻¹

Scheftner MoguCera C Disc

CoCr alloy in disc form for milling metal structures for crown and bridge frameworks.

Technical Specifications:

• Composition: Co-65%, Cr-28%, Mo-5%, Mn-1%
• Tensile strength: 597 MPa
• Vickers hardness: 288 HV10
• CTE: 114.8x10⁻⁶K⁻¹

Sheftner Starbond Ti5 Disc

This is a Ti5 type alloy in disc form for milling. It is designed for the production of implant-supported work such as bars and suprastructures but also for milling crowns and bridges.

Technical Specifications:

• Composition: Ti - 89.4%, Al 6.2%, V 4.0%, Others <1%
• Yield strength (Rp0.2): 900 MPa
• Tensile strength: 930 MPa
• Elongation at break: 10%
• Vickers hardness: 330 HV 5/30
• Density: 4.4 g/cm³
• CTE: 10.3 um/m * 10-6 K-1

PoliDent PMMA Multilayer Disc

Multilayer PMMA material in disc form for milling designed for temporary crowns and bridges.

Technical Specifications:

• Vickers hardness: min 26 HV
• Flexural strength: min. 114 MPa
• E modulus: min. 2771 MPa
• Available colors: A1, A2, A3, B1, D2

PoliDent PMMA Disc MONO

This is a monochromatic PMMA material used for making temporary crowns and bridges and for making try-in structures before making final work.

Technical Specifications:

• Vickers hardness: min 26 HV
• Flexural strength: min. 114 MPa
• E modulus: min. 2771 MPa
• Residual monomer <1%
• Available colors: A1, A2, A3, B1, B2, B3, BL1, BL2, BL3